insulated AIN aluminio aluminiumnitrid ceramic base spacer

insulated AIN aluminio aluminiumnitrid ceramic base spacer

Reputation depends on quality,  quality comes from Hard!

Aluninum Nitride Ceramic:

Aluminum nitride ceramic organic substances such as oil, grease and even fingerprints will become the source of local corrosion. Since these substances can act as a barrier, they will affect the chemical and electrochemical cleaning effect, so they must be thoroughly cleaned up. ASTM A380 has a simple water break (WATERBREAK) test to detect organic pollutants. During the test, water was poured from the top of the vertical surface. During the downward flow, the water would separate around the organic matter. Flux and/or acid chemical cleaning agent can remove oil and grease. When the tape and protective paper are removed, a part of the adhesive will always remain on the stainless steel surface. If the adhesive is not hard, it can be removed with an organic flux. However, when exposed to light or air, the adhesive hardens and forms a source of crevice corrosion. Then it needs to be cleaned mechanically with fine abrasives. The effects of these pollutants are similar to those of oil and grease. It is recommended to use a clean brush and clean water or alkaline detergent for washing, or use high-pressure water or steam to rinse. The stainless steel whose structure is mainly ferrite in use. The chromium content is between 11% and 30%, and it has a body-centered cubic crystal structure. This kind of steel generally does not contain nickel, and sometimes contains a small amount of Mo, Ti, Nb and other elements. This kind of steel has the characteristics of large thermal conductivity, small expansion coefficient, good oxidation resistance, and excellent stress corrosion resistance. It is mostly used to make atmospheric resistance. , Water vapor, water and oxidizing acid corroded parts. This type of steel has disadvantages such as poor plasticity, significantly reduced plasticity and corrosion resistance after welding, which limits its application. The application of out-of-furnace refining technology (AOD or VOD) can greatly reduce interstitial elements such as carbon and nitrogen, which makes this type of steel widely used.

Using AIN ceramics for heat resistance, melt erosion and thermal shock resistance, GaAs crystal crucible, Al evaporating dish, magnetic fluid power generation device and high temperature turbine corrosion resistant parts can be fabricated, and its optical properties can be used as an infrared window. The aluminum nitride film can be made into a high frequency piezoelectric element, a very large scale integrated circuit substrate, or the like.
Aluminum nitride heat-resistant, resistant to molten metal erosion, stable to acid, but easy to be eroded in alkaline solution. The AIN fresh surface is exposed to moist air and reacts to form a very thin oxide film. By utilizing this property, it can be used as a crucible and a die-casting mold material for smelting metals such as aluminum, copper, silver, and lead. AIN ceramics have good metallization properties and can be widely used in the electronics industry as an alternative to toxic cerium oxide.

Data Sheet:

Ø (1) high thermal conductivity (about 320W / m · K), close to BeO and SiC, more than 5 times that of Al2O3;
Ø(2) The thermal expansion coefficient (4.5×10-6°C) is matched with Si (3.5-4×10-6°C) and GaAs (6×10-6°C);
Ø (3) excellent electrical properties (dielectric constant, dielectric loss, volume resistivity, dielectric strength);
Ø(4) good mechanical properties, higher flexural strength than Al2O3 and BeO ceramics, can be sintered at normal pressure;
Ø (5) good optical transmission characteristics;
Ø(6) non-toxic;

Application industry:

 Aluminum nitride powder has high purity, small particle size and high activity, and is the main raw material for manufacturing high thermal conductivity aluminum nitride ceramic substrate.
Aluminum nitride ceramic substrate, high thermal conductivity, low expansion coefficient, high strength, high temperature resistance, chemical corrosion resistance, high resistivity, small dielectric loss, is an ideal large-scale integrated circuit heat sink substrate and packaging materials.

7.MOQ is not limited, small quantity is welcome.

8.Vigorous team and good after-sales service

Products Show

FAQ

Q: Are you trading company or manufacturer ?
A: We are factory.
 
Q: How long is your delivery time?
A: Generally it is 5-10 days if the goods are in stock. or it is 15-30 days if the goods are not in stock, it is according to quantity.
 
Q: Do you provide samples ? is it free or extra ?
A: Yes, we could offer the sample for free charge but do not pay the cost of freight.
Q: What is your terms of payment ?

A: Payment<=1000USD, 100% in advance. Payment>=1000USD, 50% T/T in advance ,balance before shippment.