Biocompatible PPSU medical grade TECASON® P MT red

Get Latest Price

Min. Order:: 1 Kilogram

Min. Order:: 1 Kilogram

Transportation:: Ocean, Land, Air, Express

Port:: Shenzhen, Guangzhou, Hongkong

Quantity:

Your message must be between 20 to 2000 characters

Contact Now

Basic Info

Supply Ability:	1000
Payment Type:	T/T,Paypal
Incoterm:	FOB,CFR,EXW,CIF,DDU
Transportation:	Ocean,Land,Air,Express
Port:	Shenzhen,Guangzhou,Hongkong

Product Description

TECASON P MT red is suitable for use in medical applications. In many medical applications, it is often desirable for designers to have a number colours to choose from when making material selection decisions. TECASON P MT red is just one of the many colour options available in this family of products.

TECASON P MT red

FACTS

Chemical designation

PPSU (Polyphenylsulfone)

Colour

red

Alternative colours available

ivory black orange green yellow grey blue brown

Density

1.31 g/cm3

MAIN FEATURES

high strength

good heat deflection temperature

biocompatible

high stiffness

resistance against high energy radiation

good chemical resistance

good weldable and bondable

hydrolysis and superheated steam resistant

TARGET INDUSTRIES

medical technology

chemical technology

mechanical engineering

electronics

food technology

automotive industry

Key Properties

Tested to The Requirements of ISO 10993

High Tensile Strength

Excellent Heat Resistance, Autoclavable

Very High Resistance to Environmental Stress

Great Mechanical Strength

High Dielectric Strength and Stability

Available in Opaque And Transparent Grades

Limitations

Attacked by Some Solvents

Poor Weatherability

Subject to Stress Cracking

Applications

Medical Device Components

Surgical Instruments

Surgical Tools

TECASON ® P MT PPSU Radel ® R Technical Data Sheet

	VALUE	UNIT	PARAMETER	NORM
Modulus of elasticity	2300	MPa	1mm/min	DIN EN ISO 527-2
(tensile test)	2300	MPa	1mm/min	DIN EN ISO 527-2
Tensile strength	81	MPa	50mm/min	DIN EN ISO 527-2
Tensile strength at yield	81	MPa	50mm/min	DIN EN ISO 527-2
Elongation at yield (tensile test)	7	%	50mm/min	DIN EN ISO 527-2
Elongation at break (tensile test)	50	%	50mm/min	DIN EN ISO 527-2
Flexural strength	107	MPa	2mm/min, 10 N	DIN EN ISO 178
Modulus of elasticity	2300	MPa	2mm/min, 10 N	DIN EN ISO 178
(flexural test)	2300	MPa	2mm/min, 10 N	DIN EN ISO 178
Compression modulus	2000	MPa	5mm/min, 10 N	EN ISO 604
Impact strength (Charpy)	n.b.	kJ/m2	max. 7,5J	DIN EN ISO 179-1eU
Notched impact strength (Charpy)	13	kJ/m2	max. 7,5J	DIN EN ISO 179-1eA
Ball indentation hardness	143	MPa		ISO 2039-1
Compression strength	18/30/66	MPa	1% / 2% / 5%	EN ISO 604
Glass transition temperature	218	C		DIN EN ISO 11357
Melting temperature	n.a.	C		DIN EN ISO 11357
Thermal conductivity	0.25	W/(k*m)		ISO 22007-4:2008
Specific heat	1.1	J/(g*K)		ISO 22007-4:2008
Service temperature	190	C	short term	NN
Service temperature	170	C	long term	NN
Thermal expansion (CLTE)	6	10-5*1/K	23-60°C, long.	DIN EN ISO 11359-1;2
Thermal expansion (CLTE)	6	10-5*1/K	23-100°C, long.	DIN EN ISO 11359-1;2
surface resistivity	1014	Ω		-
volume resistivity	1014	Ω*cm
Resistance to hot water/ bases	+	-		-
Flammability (UL94)	V0	-	listed (value at 0.79mm)	DIN IEC 60695-11-10;
Resistance to weathering	-	-		-
Water absorption	0.1 - 0.2	%	24h / 96h (23°C)	DIN EN ISO 62

Send your message to this supplier

* From:
* To:

Ms. Tina
* Messages:

Enter between 20 to 4,000 characters.

Related Keywords

TECASON P MT PPSU Radel R , TECASON P MT Sheet Rod , Polysulfone PSU PPSU