High Hardness DIN 1.3343 High Speed Tool Steel Rod
- Payment Type:
- T/T, Western Union
- Incoterm:
- CFR
- Min. Order:
- 500 Kilogram
- Min. Order:
- 500 Kilogram
- Delivery Time:
- 7 Days
- Transportation:
- Ocean, Land, Air
Quantity:
Your message must be between 20 to 2000 characters
Contact NowBasic Info
Basic Info
| Place of Origin: | shenzhen |
|---|---|
| Productivity: | 1000 ton per month |
| Supply Ability: | 1000 ton per month |
| Payment Type: | T/T,Western Union |
| Incoterm: | CFR |
| Transportation: | Ocean,Land,Air |
Product Description
Product Description
High Hardness DIN 1.3343 High Speed Tool Steel Rod
Forging ¢ 50 ~ ¢ 300 MM DIN 1.3343 High Speed Tool Steel Rod
Description:
1.AISI M2/DIN 1.3343/S6-5-2/ JIS SKH 51/GB W6Mo5Cr4V2 High speed steel round bar
2.Forged condition, annealing or harden, black or milled surface
3. Forged technology: EAF+LF+VD+ESR+Forging +Q T + Machined surface
4.E7.Production leadtime: 7~30 days
5. Chemical composition:
7.Compared grades(based on usage)
Applications:
Used in the manufacture of various types of general tools, and therefore can be produced under
high load wear-resistant parts, such as cold extrusion die. Has high hardness, high wear resistance,
high fever hard, high hardenability and sufficient ductility and toughness, good casting, forging,
weldingand machining performance and tool steel, and thus it occupies and important position.
Specifications:
Competitive Advantage:
high strength at elevated temperatures
good toughness
high compressive strength
International general tungsten molybdenum high-ductility high-speed steel. The carbon granule of this
steel is fine and even, featuring in high ductility, superior cutting performance and good heat plasticity
Good resistance to abrasions, particularly superior read hardness under 600`C.
Competitive price
Fast production leadtime
Forging ¢ 50 ~ ¢ 300 MM DIN 1.3343 High Speed Tool Steel Rod
Description:
1.AISI M2/DIN 1.3343/S6-5-2/ JIS SKH 51/GB W6Mo5Cr4V2 High speed steel round bar
2.Forged condition, annealing or harden, black or milled surface
3. Forged technology: EAF+LF+VD+ESR+Forging +Q T + Machined surface
4.E7.Production leadtime: 7~30 days
5. Chemical composition:
|
C |
Si |
Mn |
Cr |
Mo |
V |
W |
P |
S |
|
0.86-0.94 |
0.40max |
0.45max |
3.80-4.50 |
4.70-5.20 |
1.70-2.20 |
5.90-6.70 |
0.03max |
0.03max |
7.Compared grades(based on usage)
|
Chinese |
American |
German |
Japanese |
|
GB |
AISI |
DIN |
JIS |
|
W6Mo5Cr4V2 |
M2 |
1.3343 |
SKH51 |
Applications:
Used in the manufacture of various types of general tools, and therefore can be produced under
high load wear-resistant parts, such as cold extrusion die. Has high hardness, high wear resistance,
high fever hard, high hardenability and sufficient ductility and toughness, good casting, forging,
weldingand machining performance and tool steel, and thus it occupies and important position.
Specifications:
|
|
Steel round bar (mm) |
|
|
|
Diameter |
Length |
|
Forged condition |
¢50~¢300 |
2500~4000 |
Competitive Advantage:
high strength at elevated temperatures
good toughness
high compressive strength
International general tungsten molybdenum high-ductility high-speed steel. The carbon granule of this
steel is fine and even, featuring in high ductility, superior cutting performance and good heat plasticity
Good resistance to abrasions, particularly superior read hardness under 600`C.
Competitive price
Fast production leadtime