Mn18Cr2 Steel Casting Ball Mill Liners For Cement Mill DF04
- Min. Order:
- 1
- Min. Order:
- 1
- Delivery Time:
- 30 Days
Your message must be between 20 to 2000 characters
Contact Now| Place of Origin: | Jiangsu, China (Mainland) |
|---|
Mn18Cr2 Steel Casting Ball Mill Liners For Cement Mill DF049
Quick Details
1.The series include Mn13, Mn13Cr2 and Mn18Cr2.
2.Materials conform to GB/T 5680-1998, DL/T 681-1999, JIS G 5153-1999, ASTM A 128.
Mn13, Mn13Cr2 and Mn18Cr2 steel casting liners for Cement Mill / Ball Mill Liners
1. Alloy: The series include Mn13, Mn13Cr2 and Mn18Cr2.
2. Application: It is applicable to the working condition of strong impact, such as teeth plates, concaves and mantles of crushers and excavator bucket teeth and mill liners for SAG mills and AG mills.
3. Microstructure: Austenite or Austenite + little Carbide
4. Hardness: Less than HB300
5. Impact Value: more than 118J
6. Tensile Strength: more than 685 Mp
7. International Standard: GB/T 5680-1998, DL/T 681-1999, JIS G 5153-1999, ASTM A 128.
Technical Parameters
| Item | Cr-Mo Alloy Steel I |
Cr-Mo Alloy Steel II |
Cr-Mo Alloy Steel III |
| C | 0.30-0.50 | 0.65-0.90 | 0.40-0.90 |
| Si | 0.50-1.20 | ≤0.75 | 0.70-1.20 |
| Mn | 0.40-1.20 | 0.50-1.20 | 0.60-1.00 |
| Cr | 1.70-2.50 | 1.50-2.50 | 4.00-7.00 |
| S | ≤0.04 | ≤0.06 | ≤0.04 |
| P | ≤0.04 | ≤0.06 | ≤0.06 |
| Mo | ≤0.5 | ≤0.5 | ≤0.5 |
| Cu | 0.10-0.60 | ≤0.25 | 0.20-0.40 |
| Ni | ≤0.50 | ≤0.30 | ≤0.30 |
| Re | ≤0.02 | ≤0.02 | ≤0.02 |
| Equivalent Specifications |
DL/T 681-1999 GB/T26651-2011 |
AS 2074 L2B Mod |
DL/T681-1999 |
| Material Type | Martensite Steel | Martensite or Pearlitic Cr Mo Steel |
Martensite Steel |
| Hardness | HRc≥48 | HB470& HB321-370 |
HRc≥50 |
| Impact Value | AK≥40J | - | AK≥10J |
| Item |
High Cr white iron |
High Cr Alloy Steel |
High Manganese Steel |
Ni-Hard cast iron |
| C | 2.40-3.20 | 1.1-2.2 | 0.90-1.30 | 2.40-3.60 |
| Si | 0.60-1.20 | 0.60-1.20 | ≤0.08 | ≤0.08 |
| Mn | 0.50-1.00 | 0.50-1.00 | 11.00-18.00 | ≤2.0 |
| Cr | 12.00-30.00 | 11.00-30.00 | 1.50-2.20 | 1.5-10.0 |
| S | ≤0.04 | ≤0.04 | ≤0.04 | ≤0.15 |
| P | ≤0.06 | ≤0.06 | ≤0.06 | ≤0.15 |
| Mo | 0.10-0.30 | 0.10-0.30 | ≤1.0 | ≤0.10 |
| Cu | 0.10-1.00 | 0.10-1.00 | - | - |
| Ni | 0-0.30 | 0-0.30 | - | 3.3-10.0 |
| Re | - | - | - | - |
| Equivalent Specifications |
GB/T 8263-1999 AS 2027 Cr27 AS 2027 CrMo15/3 AS 2027 CrMo20/2/1 ASTM A532 Class III type A25%Cr ASTM A532 Class II type B15%Cr-Mo BS 4844 3E DIN1695 NFA32401 |
BG/T 5680-1998 DL/T 681-1999 JIS G 5153-1999 ASTM A 128 DIN GX120Mn12 AFNOR:Z120Mn12 |
GB/T 8263-1999 AS 2027/Ni-Cr1-550 AS 2027/Ni-Cr2-500 AS 2027/Ni-Cr4-500 AS 2027/Ni-Cr4-600 AS 2027/Ni-Cr4-630 ASTM A 532 1-A,B,C,D ASTM A 532 2-A,B,C,D,E ASTM A 532 3-A |
|
| Material Type | Martensite matrix | Austenitic Mn Steel | - | |
| Hardness | HRc≥56 | HB≤300 | HRc≥56 | |
| Impact Value | AK≥4J | AK≥80J | - | |