RTV-2 Molding Silicon Rubber for Candle Molds Making

RTV-2 Molding Silicon Rubber for Candle Molds Making (625#) applications:

Liquid silicone rubber for brushing mold making is for toy gifts and craftwork gift, products with complex fine details, Poly technique, lightings, candles, and molds in multiple pieces for large products and made in pouring way
RTV-2 Molding Silicon Rubber for Candle Molds Making description:

Liquid silicone rubber for brushing mold making is mainly used for toy gifts and craftwork gifts with the advantages of good tensile strength, high tear strength, high temperature resistance, high duplication times and repeated use, etc. It is suitable for small products or fine and precision products which is difficult to demould. This silicone rubber is one of the products with the highest use level in the production of craftwork gifts and the shrinkage is up to 0.2%.

RTV-2 Molding Silicon Rubber for Candle Molds Making operation instruction:

The product is white or red flowing liquid with general hardness of 2250A° After curing. If the customer wants to make large products and large size molds, the mold should be made of silicone rubber with high hardness. On the contrary, if the mold with fine and precision patterns, it should be made of silicon with low hardness. The amount of the curing agent depends on the actual requirements of the customer. If molds requiring fast drying and demould, more curing agent is needed; Contrarily, if molds requiring slower drying and demould, less curing agent is needed.

(Note: Our company does not recommend you to add silicone oil. If a special soft silicon mold or fine detailed and complex patterns products are required, 5%-10% silicone oil can be added to soften the mold for easy demould. )

The proportions and reactions of the curing agent and the silicon are listed as follows:

1. Adding curing agent 1%, the silicone can still be operated within 2.5 hours and can be demoulded after 6-8 hours.

2. Adding curing agent 2%, the silicone can still be operated within 50 minutes to 1 hour and can be demoulded after 2-3 hours.

3. Adding curing agent 3%, the silicone can still be operated within 28 - 30 minutes and can be demoulded after 1.5-2 hours.

4. Adding curing agent 4%, the silicone can still be operated within 10 - 15 minutes and can be demoulded after 1 -1.5 hours.

We can provide you the best quality concrete craftworks molding siliconen rubber with competitive price and free demold technology.

Need any help on silicone rubber, please feel free to contact Hugo:

TEL:086-755-89948019

FAX:086-755-89948030

MOBILE:086-13428680288

SKYPE: hugo.chen007

Website:www(dot)szrl(dot)net

E-MAIL:hyhc@szrl.net