buy liquid molding rtv2 silicone rubber for plaster crafts

Mixing Ratio for Silicon Rubber & Curing Agent and the reaction time (Under room-temperature-25 0C)
1,Added with 2% of curing agent, silicon can still flow within 2.5 hours, mold can be released in 8-10 hours.
2,Added with 3% of curing agent, silicon can still flow within 1.1 to 1.2 hours, mold can be released in 6-8 hours.
3,Added with 4% of curing agent, silicon can still flow within 55-60 minutes, mold can be released in 4-6 hours.
4,Added with 5% of curing agent, silicon can still flow wtithin 45-50 minutes, mold can be released in 4 hours.

Why could the silicone mold be reused only for a few times?

It can be due to the following reasons: 

a. Adding too much silicone oil in to silicon rubber. Silicon oil is an additive which destroies the molecular weight 

of silicone rubber and reduce the tension and tear strength.

b. Using the silicon rubber with a high hardness to make molds for small sized products with delicate and intricate 

designs and the silicon rubber with a low hardness to makes molds for large sized products with simple designs. 

(Notes: we should choose the silicon rubber specifically according to the requirements of our products to avoid 

this problem.)

How to make silicone molds by yourself?

SHELF LIFE of liquid molding rtv2 silicone rubber

Twelve (12) months from date of shipment when stored at 24°C in original unopened packages.

PACKAGE for liquid molding rtv2 silicone rubber:

Packed in clean 25kg/pail,  200kg/pail.